| 性能项目 | 试验条件[状态] | 测试数据 | 测试方法 | 数据单位 | ||
| 物理性能 | 比重 | 1.99 | ASTM D792 | ISO 1183/A | g/cm3 | |
| 成型收缩率 | Flow:3.18mm | 0.20 | ％ | |||
| Across Flow:3.18mm | 0.60 | ％ | ||||
| 吸水率 | 24hr,23℃ | 0.020 | ASTM D570 | ％ | ||
| 机械性能 | 拉伸应力 | 130 | ISO 527-2 | MPa | ||
| yield | 131 | ASTM D638 | MPa | |||
| 断裂伸长率 | yield | 1.0 | ASTM D638 | ％ | ||
| yield | 0.80 | ISO 527-2 | ％ | |||
| 弯曲模量 | 19300 | ASTM D790 | MPa | |||
| 19000 | ISO 178 | MPa | ||||
| 弯曲强度 | 214 | ASTM D790 | MPa | |||
| 200 | ISO 178 | MPa | ||||
| 抗压强度 | 262 | ASTM D695 | MPa | |||
| 265 | ISO 604 | MPa | ||||
| IZOD 缺口冲击强度 | 3.18mm | 53.4 | ASTM D256 | J/m | ||
| ISO 180/A | kjm2 | |||||
| IZOD 无缺口冲击强度 | 3.18mm | 214 | ASTM D256 | J/m | ||
| ISO 180 | kjm2 | |||||
| 热性能 | 热变形温度 | 1.8MPa,Annealed | ＞260 | ASTM D648 | ISO 75-2/A | ℃ |
| 热传导 | 0.59 | W/m/K | ||||
| 阻燃等级 | V-0 | UL 94 | ||||
| 电气性能 | 介电强度 | 16 | ASTM D149 | kV/mm | ||
| 介电常数 | 26℃,1000Hz | 4.90 | ASTM D150 | |||
| 26℃,1E Hz | 4.80 | ASTM D150 | ||||
| 损耗因子 | 26℃,1000Hz | 0.004 | ASTM D150 | |||
| 26℃,1E Hz | 0.002 | ASTM D150 | ||||
| 耐电弧 | 185 | sec | ||||
其他新闻
- (PBT沙伯基础) 沙伯基础全系列 2024-04-17
- (旭化成PA66) 旭化成PA66全系列 2024-04-17
- (罗地亚PA66) 罗地亚PA66全系列 2024-04-17
- (首诺PA66) 首诺PA66全系列 2024-04-17
- 沙伯基础PA66 沙伯基础PA66全系列 2024-04-17
- (朗盛PA66) 朗盛PA66全系列 2024-04-17
- (东丽PA66) 东丽PA66全系列 2024-04-17
- 美国杜邦 杜邦全系列 2024-04-17
- 美国沙伯基(PBT沙伯基础全系列) 2024-04-17
- 瑞士EMS(PA66瑞士全系列) 2024-04-17
- 日本旭化成(PA66尼龙全系列) 2024-04-17
- 日本东丽(PA66尼龙全系列) 2024-04-17
- 法国罗地亚(PA66聚酰胺)全系列 2024-04-17
- 德国巴斯夫(PA66聚酰胺)全系列 2024-04-17
- 德国朗盛(PA66德国朗盛)全系列 2024-04-17
联系方式
- 地址：苏州 昆山市陆家镇仕泰隆模具城13号
- 联系电话：未提供
- 联系人：李颖
- 手机：13564996490
- 微信：13564996490
- QQ：2087429965
- Email：2087429965@qq.com
产品分类
站内搜索